ASTM C533硅酸钙绝热板和绝热管标准规范
ASTM C533硅酸钙绝热板和绝热管标准规范—标准名称
ASTM C533 Standard Specification for Calcium Silicate Block and Pipe Thermal Insulation
ASTM C533硅酸钙绝热板和绝热管标准规范
ASTM C533硅酸钙绝热板和绝热管标准规范—适用范围
Scope:
This specification covers calcium silicate block and pipe thermal insulation for use on surfaces with temperatures between 80 and 1700℉(27 to 927℃) , unless otherwise agreed upon between the manufacturer and the purchaser. The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only. The following safety hazards caveat pertains only to the test method (section 12) described in this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM C533硅酸钙绝热板和绝热管标准规范—测试项目和方法
ASTM C303 Dimension and Density尺寸和密度
ASTM C203 Flexural strength 弯曲强度
ASTM C165 Procedure A Compressive strength, at 5% deformation 抗压强度
ASTM C421 Mass loss by tumbling after first 10 minutes 前10分钟翻转损失
ASTM C421 Mass loss by tumbling after second 10 minutes后10分钟翻转损失
ASTM C356 Soaking heat linear shrinkage (Specified temperature) 线性收缩(指定温度)
ASTM C411 Hot surface performance (Specified temperature) 热面性能试验(指定温度)
ASTM C1045 ASTM C518 ASTM C177 Apparent thermal conductivity 表观导热系数
ASTM E84 Surface burning characteristics表面燃烧
ASTM E136 Non-combustibility 不燃性测定
ASTM C795(包括以下两个标准) Stress corrosion performance 应力腐蚀性能(Type I only)
ASTM C692 External Stress Corrosion Cracking Tendency of Austenitic Stainless Steel 对奥氏体不锈钢应力腐蚀裂纹扩展影响
ASTM C871 Leachable Chloride, Fluoride, Silicate, and Sodium Ions, pH Value Cl-, F-, SiO32-, Na+含量pH 值
ASTM C1617 Mass loss corrosion Rate(Type I only) 质量损失腐蚀速率
ASTM C1616 Moisture content 含水量
----------------------------------------------------------------------------------------------------------------------
----------------------------------------------------------------------------------------------------------------------