物理安全检测
ASTM D3039／D3039M 聚合物基复合材料拉伸性能试验方法
ASTM D3039／D3039M 聚合物基复合材料拉伸性能试验方法—标准名称
ASTM D3039／D3039M Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials
ASTM D3039／D3039M 聚合物基复合材料拉伸性能试验方法—适用范围
Scope:
This test method determines the in-plane tensile properties of polymer matrix composite materials reinforced by high-modulus fibers. The composite material forms are limited to continuous fiber or discontinuous fiber-reinforced composites in which the laminate is balanced and symmetric with respect to the test direction
ASTM D3039／D3039M 聚合物基复合材料拉伸性能试验方法—引用文件
ASTM D792 Test Methods for Density and Specific Gravity (Relative Density) of Plastics by Displacement
ASTM D883 Terminology Relating to Plastics
ASTM D2584 Test Method for Ignition Loss of Cured Reinforced Resins
ASTM D2734 Test Methods for Void Content of Reinforced Plastics
ASTM D3171 Test Methods for Constituent Content of Composite Materials
ASTM D3878 Terminology for Composite Materials
ASTM D5229/D5229M Test Method for Moisture Absorption Properties and Equilibrium Conditioning of Polymer Matrix Composite Materials
ASTM E4 Practices for Force Verification of Testing Machines
ASTM E6 Terminology Relating to Methods of Mechanical Testing
ASTM E83 Practice for Verification and Classification of Extensometer Systems
ASTM E111 Test Method for Young’s Modulus, Tangent Modulus, and Chord Modulus
ASTM E122 Practice for Calculating Sample Size to Estimate, With Specified Precision, the Average for a Characteristic of a Lot or Process
ASTM E132 Test Method for Poisson’s Ratio at Room Temperature
ASTM E177 Practice for Use of the Terms Precision and Bias in ASTM Test Methods
ASTM E251 Test Methods for Performance Characteristics of Metallic Bonded Resistance Strain Gauges
ASTM E456 Terminology Relating to Quality and Statistics
ASTM E1012 Practice for Verification of Testing Frame and Specimen Alignment Under Tensile and Compressive Axial Force Application
ASTM E1237 Guide for Installing Bonded Resistance Strain Gages
----------------------------------------------------------------------------------------------------------------------
----------------------------------------------------------------------------------------------------------------------